Product Data and Information
CF-3001
| General Purpose, Variable Flexibility, High Impact Strength Adhesive | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-3001 | |||||||
| Description: | CF-3001 is an epoxy-based, room temperature cure, variable flexibility adhesive. CF-3001 has excellent resistance to mechanical impact and shock, low shrinkage during cure, and good electrical properties. This adhesive is recommended for bonding many different materials, wood, aluminum, steel, glass, di-allyl, phenolic, etc. | |||||||
| Specification: | Part A | Part B | ||||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: |
Amber 10-12,000 cps 1.16 12 months |
Dark Amber 40-50,000 cps 0.95 12 months |
||||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) Tensile shear (Aluminum to Aluminum) | |||||||
|
-300 °F -100 °F RT +160 °F +200 °F Hardness Shore D @ 50/50 Coef. Of thermal expansion Thermal shock per Mil-I-16923 Mechanical shock per Mil-I-16923 |
2000 psi 2400 psi 3000 psi 600 psi 300 psi 90 4.4 x 10-5 in/in/ °F Passes all cycles 227 in. lbs. |
|||||||
| Curing Procedure: |
1. Clean thoroughly all surfaces to be bonded 2. Mix uniformly, using the selected ratio 3. Apply a thin layer of material to the pieces to be bonded, and position together 4. Cure, using appropriate cure cycle |
|||||||
|
Mix Ratio By Weight: Part A/Part B Pot life: Viscosity: Cure Cycle: |
Hard 3/1 to Soft 1/3 60 min + 18,000 – 30,000 cps 24 hrs @ RT or 1 hr @ 150 °F or 20 min @ 200 °F |
|||||||
| Cured Properties: | Appearance of material will appear matte to glossy. | |||||||
| Waste Disposal: | Allow to cure 24 hrs @ RT. Material is now inert and may be disposed of in a normal landfill. | |||||||
CF-3003 Natural
| Fast Heat Cure, Medium Pot Life Adhesive/Potting Compound | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-3003 Natural | |||||||
| Description: | CF-3003 NATURAL is a thixotropic, medium-pot life adhesive that cures quickly at elevated temperatures. It has found wide use as an adhesive for neoprene rubber, glass-filled nylon, di-allyl, phenolic, epoxy molded parts, and many plated metals. The long working time and short elevated cure recommend its use for automatic and semi-automatic applications. | |||||||
| Specification: | Part A | Part B | ||||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: Shelf Life - Premixed Frozen |
Brown Thixotropic 1.9 12 months 3 months @ -40 °F Part A and B mixed |
Amber 640 cps 0.95 12 months |
||||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) Tensile shear (Aluminum to Aluminum) | |||||||
|
-65 °F +75 °F +190 °F Hardness Shore Thermal expansion Linear shrinkage Dielectric strength Thermal conductivity (BTU)(in)/(hr)(ft2)(°F) |
2000 psi 2400 psi 1000 psi D 85 Min in/in/per °F 22x10 -6 .001 in/in/ °C 450 volts/mil 4.6 |
|||||||
| Curing Procedure: |
1. Clean thoroughly all surfaces to be bonded 2. Mix uniformly, 100 pts A with 11.5 pts B 3. Apply a thin layer of material to the pieces to be bonded, and position together. 4. Cure, using appropriate cure cycle |
|||||||
|
Mix Ratio by weight: Pot life: Viscosity: Cure cycle: Premixed frozen |
100 pts A with 11.5 pts B 60 min + Thixotropic 24 hrs @ RT or 1 hr @ 150 °F or 20 min @ 200 °F Thaw to RT, apply, and cure |
|||||||
| Cured Properties: |
Appearance of material will appear matte to glossy. (with amber hue) Operating Temp. -40 °F to 400 °F |
|||||||
| Waste Disposal: | Allow to cure 24 hrs @ RT. Material is now inert and may be disposed of in a normal landfill. | |||||||
CF-3003-80
| Fast Heat Cure, Medium Pot Life Adhesive/Potting Compound | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-3003-80 | |||||||
| Description: | CF-3003-80 is a high-viscosity, medium-pot life adhesive that cures quickly at elevated temperatures. It has found wide use as an adhesive for neoprene rubber, glass-filled nylon, di-allyl, phenolic, epoxy molded parts, and many plated metals. The long working time and short elevated cure recommend its use for automatic and semi-automatic applications. | |||||||
| Specification: | Part A | Part B | ||||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: Shelf Life - Premixed Frozen |
Black 115-125,000 cps 1.85 12 months 3 months @ -40 °F Part A and B mixed |
Amber 640 cps 0.95 12 months |
||||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) Tensile shear (Aluminum to Aluminum) | |||||||
|
-65° F +75° F +190° F Hardness Shore Thermal expansion Linear shrinkage Dielectric strength |
2000 psi 2400 psi 1000 psi D 85 Min in/in/per ° F 22x10 -6 .001 in/in/ °C 450 volts/mil |
|||||||
| Curing Procedure: |
1. Clean thoroughly all surfaces to be bonded 2. Mix uniformly, 100 pts A with 12.4 pts B 3. Apply a thin layer of material to the pieces to be bonded, and position together 4. Cure, using appropriate cure cycle |
|||||||
|
Mix Ratio by weight: Pot life: Viscosity: Cure cycle: Premixed frozen |
100 pts A with 12.4 pts B 60 min + 15,000 – 20,000 cps 24 hrs @ RT or 1 hr @ 150° F or 20 min @ 200° F Thaw to RT, apply, and cure |
|||||||
| Cured Properties: |
Appearance of material will appear matte to glossy. (with amber hue) Operating Temp. -40 °F to 400 °F |
|||||||
| Waste Disposal: | Allow to cure 24 hrs @ RT. Material is now inert and may be disposed of in a normal landfill. | |||||||
CF-3009
| Rapid Cure Two-Component Adhesive | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-3009 | |||||||
| Description: | CF-3009 is a rapid room-temperature curing epoxy adhesive. Designed for bonding a wide range of materials, CF-3009 has excellent resistance to mechanical impact and shock. | |||||||
| Specification: | Part A | Part B | ||||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: |
Clear 100% 12,000 cps 12 months |
Red 100% 13,000 cps 12 months |
||||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) Tensile shear | |||||||
|
Cured @ 75 ° F Hardness shore D Cured @ 75 ° F Cured @ RT 7 Days + 2 hr water boil Water absorption - Weight % 7 Days @ 75 ° F + 24 hrs in water |
30 minutes 2 hours 10 min 20 min 30 min 01 hour 24 hours 0.33 |
1,000 psi 1,500 psi 35 55 67 72 79 72 |
||||||
| Curing Procedure: |
1. Clean thoroughly all surfaces to be bonded 2. Mix uniformly, 50 parts A with 50 parts B 3. Apply a thin layer of material to the pieces to be bonded, and position together 4. Cure, using appropriate cure cycle |
|||||||
|
Mix Ratio: Part A / Part B Work life @ 25 ° F: |
50/50 3-4 min |
|||||||
| Cured Properties: | Appearance of the material will appear satin clear. | |||||||
| Waste Disposal: | Any mixed material is inert after being cured for approx. 10 - 20 min. | |||||||
CF-3304
| Medium Viscosity, Fast Heat Cure, Medium Pot Life Adhesive | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-3304 | |||||||
| Description: | CF-3304 is a medium viscosity, medium pot life adhesive that cures quickly at elevated temperatures. CF-3304 has found wide use as an adhesive for neoprene rubber, glass-filled nylon, Di-allyl, Phenolic, epoxy molded parts, and engineered plastic parts. The long working time and short elevated cure recommended the use of CF-3304 for automatic and semi-automatic applications. | |||||||
| Specification: | Part A | Part B | ||||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: |
Amber 12,000 cps 1.16 12 months |
Amber 640 cps 0.95 12 months |
||||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) Tensile shear (Aluminum to Aluminum) | |||||||
|
-65° F -75° F +190° F Hardness Shore D Coef. Of thermal expansion Thermal shock per Mil-I-16923 Mechanical shock per Mil-I-16923 |
2000 psi 2400 psi 1000 psi 90 4.4 x 10-5 in/in/ ° F Passes all cycles 175 in. lbs. |
|||||||
| Curing Procedure: |
1. Clean thoroughly all surfaces to be bonded 2. Mix uniformly, 100 parts A with 25 parts B by weight 3. Apply a thin layer of material to the pieces to be bonded, and position together. 4. Cure, using appropriate cure cycle. |
|||||||
|
Mix Ratio by weight: Pot life: Viscosity: Cure cycle: |
100/25 60 min + 5,000 cps 24 hrs @ RT or 1 hr @ 150° F or 20 min @ 200° F |
|||||||
| Cured Properties: | Appearance of material will appear matte to glossy. | |||||||
| Waste Disposal: | Allow to cure 24 hrs @ RT. Material is now inert and may be disposed of in a normal landfill. | |||||||
CF-4300
| Very Low Viscosity, Encapsulation/Potting Impregnating Compound | ||||||||
|---|---|---|---|---|---|---|---|---|
| Product: | CF-4300 | |||||||
| Description: | CF-4300 is a very low viscosity, 100% solids epoxy encapsulation/potting resin. Of particular importance is CF-4300 ability to quickly wet out and impregnate all types of electronic coils, transformers, etc. Long pot life, medium temperature cure cycle, good mechanical and thermal impact strength, recommended as a general-purpose electronic material. CF-4300 meets the requirements of MIL-I-16923. | |||||||
| Specification: | Part A | Part B | Part C | |||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: Solids: |
Light Amber 10 - 12,000 cps 1.15-1.17 12 months 100% |
Amber 75 150 cps 1.35 12 months 100% |
Dark Amber 600-800 cps 0.98 |
|||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) | |||||||
|
Density Lb/cu.in Tensile strength Flexural strength Compressive strength Hardness Shore D Coef. Of thermal expansion Linear shrinkage % Heat distortion temp. |
.043 11,500 psi. 21,200 psi. 16,800 psi 89 35 x 10 to the -6 .5 250 ° C |
|||||||
| ELECTRICAL PROPERTIES: | K | D | ||||||
|
100Hz. @ 25 ° C 100K Hz. @ 25 ° C Dielectric Strength -Volts/mil. |
3.28 3.03 |
.008 .014 475 |
||||||
| Curing Procedure: |
1. If either Part A or Part B is cloudy or crystallized, warm to 180–250 ° F until clear, and cool to room temperature. 2. Mix equal parts A and B with .5% C 3. Cure, using appropriate cure cycle |
|||||||
|
Mix Ratio By Weight: A/B/C Pot life: Cure cycle |
100/100/.5 12-36 Hrs. @ 25 ° C 2-4 Hrs. @ 250 ° F following a post-cure of 6-12 Hrs. @ 350 ° F or 1-2 Hrs. @ 300 ° F following a post-cure of 6-12 Hrs. @ 350 ° F |
|||||||
| Cured Properties: | ||||||||
| Waste Disposal: | Allow to cure for 2-4 Hrs. @ 250 ° F. Material is now inert and may be disposed of in a normal landfill. | |||||||
CF-4301
| Medium Viscosity, Fast Room Temperature Cure, Potting/Encapsulation | ||||||
|---|---|---|---|---|---|---|
| Product: | CF-4301 | |||||
| Description: | CF-4301 is a 100% solids epoxy-based potting compound. Designed to cure quickly at low temperatures. CF-4301 is recommended for encapsulating all types of electronic components. | |||||
| Specification: | Part A | Part B | ||||
|
Color: Viscosity: Sp. Gravity: Shelf Life: Solids: |
Black 80,000 cps 1.50-1.65 12 months 100% |
Clear 100 .98 12 months 100% |
||||
| Physical Properties: | (Typical values, not intended for use in preparing specifications) | |||||
|
Density Lb/cu.in Tensile strength Flexural strength Compressive strength Hardness Shore D Coef. Of thermal expansion Linear shrinkage in/in Heat distortion temp. |
.057 9,000 psi. 15,000 psi. 17,000 psi 92 28 x 10 to the -6 .006 100 ° C |
|||||
| ELECTRICAL PROPERTIES: | @ 30° C | @ 150° C | ||||
| K | D | K | D | |||
|
100Hz. 100K Hz. Vol. resistivity Dielectric Strength -Volts/mil. |
4.62 4.20 3.33 x 10 to the 14th 500 |
.017 .031 |
5.97 4.99 450 |
.158 .023 |
||
| Curing Procedure: |
1. Stir part A thoroughly, de-air if possible 2. Add part B to part A, mix and de-air 3. Cure, using the most convenient cure cycle. |
|||||
|
Mix Ratio by weight: A/B/C Pot life: Cure cycle |
100/6 30 min. @ 25 ° C 24 Hrs. @ 25 ° C or 2 Hrs. @ 60 ° C |
|||||
| Cured Properties: | Appearance of material will appear matte to glossy. | |||||
| Waste Disposal: | Allow to cure 24 hrs @ RT. Material is now inert and may be disposed of in a normal landfill. | |||||
The information herein is based on data obtained from our own research and is considered accurate. However, no warranty is expressed or implied regarding the accuracy of these data, the results to be obtained from the use thereof, or that any such use will not infringe any patent. This information is furnished upon the condition that the person receiving it shall make his own tests to determine the suitability thereof for his particular purpose.